PH range | 0-14 |
Maximum service temperature/°C | Na type≤120;H type≤100 |
Expansion Rate/% | ( Na +→H +)≤10 |
Industrial resin layer height/m | 1.0-3.0 |
Regeneration liquid concentration/%: | NaCl: 4-10; HCl:2-5; H2SO4:1-2;2-4 |
Regeneration liquid dosage (100%) / Kg/m3 (Wet resin) | NaCl(industry): 75-150; HCl(industry):40-100; H2SO4(industry): 75-150; |
Regeneration liquid flow rate m/h | 5-8 |
Regeneration contact time/min | 30-60 |
Washing flow ratem/h | 10-20 |
Washing time/min | about 30 |
Working flow rate m/h | 10-40 |
Working exchange capacity mmol/l (Wet resin) | NaCl Regeneration≥800-1000; HCl Regeneration≥1000-1300 |
Appearance: | white or golden global granule |
PH range | 1-14 |
Maximum service temperature/°C | OH type ≤40°C, Cl type ≤80°C |
Shaping dilatability% | (Cl-→OH-)≤18-22 |
Resin height | ≥1.5m |
Regeneration liquid concentration: | NAOH:4-5% |
Regeneration liquid dosage | volume:resin volume =3-5:1 |
Regeneration liquid flow rate | 4-6m/h |
Regeneration contact time | 60min |
Washing flow rate | 15-25m/h |
Washing time | about 20min |
Working flow rate m/h | 15-25m/h |
PH range | 0-14 |
Maximum service temperature/°C | Na+ , <120℃; H+ , <100℃ |
Expansion Rate/% | ( Na +→H +)≤10 |
Industrial resin layer height/m | 1.0-3.0 |
Regeneration liquid concentration/%: | HCl:2-5; H2SO4:1-2;2-4 |
Regeneration liquid dosage (100%) / Kg/m3 (Wet resin) | Cl(industry):40-100; H2SO4(industry): 75-150; |
Regeneration liquid flow rate m/h | 5-8 |
Regeneration contact time/min | 30-60 |
Washing flow ratem/h | 10-20 |
Washing time/min | about 30 |
Working flow rate m/h | 10-40/80-100 |
Working exchange capacity mmol/l (Wet resin) | ≥1300 |
PH range | 0-9 |
Maximum service temperature/°C | ≤100 |
Expansion Rate/% | ( OH- →CL- )≤35 |
Industrial resin layer height/m | M1.0-3.0 |
Regeneration liquid concentration/% | NAOH:2.0-4.0 |
Regeneration liquid dosage (100%) / Kg/m3 (Wet resin) | NAOH:40-70 |
Regeneration liquid flow rate m/h | 4-6 |
Regeneration contact time/min | 30-50 |
Washing flow ratem/h | 15-25 |
Washing time/min | about 25 |
Working flow rate m/h | 15-25 |
Working exchange capacity mmol/l (Wet resin) | MMOL/L(Wet resin)≥950 or Adsorption amount of hexavalent chromium G/L(Wet resin)≥75 |
PH range | 0-9 |
Maximum service temperature/°C | ≤100 |
Expansion Rate/% | ( OH- →CL- )≤35 |
Industrial resin layer height/m | M1.0-3.0 |
Regeneration liquid concentration/% | NAOH:2.0-4.0 |
Regeneration liquid dosage (100%) / Kg/m3 (Wet resin) | NAOH:40-70 |
Regeneration liquid flow rate m/h | 4-6 |
Regeneration contact time/min | 30-50 |
Washing flow ratem/h | 15-25 |
Washing time/min | about 25 |
Working flow rate m/h | 15-25 |
Working exchange capacity mmol/l (Wet resin) | MMOL/L(Wet resin)≥950 or Adsorption amount of hexavalent chromium G/L(Wet resin)≥75 |
PH range | 5-14 |
Maximum service temperature/°C | ≤100 |
Expansion Rate/% | ( H +→Na +)≤65 |
Industrial resin layer height/m | M0.8-2.0 |
Regeneration liquid concentration/% | HCL:3-6 H2SO4:0.5-1 |
Regeneration liquid dosage (100%) / Kg/m3 (Wet resin) | HCL 40-60 H2SO4 80-120 |
Regeneration liquid flow rate m/h | HCL:4-8 H2SO4:10-25 |
Regeneration contact time/min | 30-50 |
Washing flow ratem/h | about 20 |
Washing time/min | 20-30 |
Working flow rate m/h | 20-40 |
Working exchange capacity mmol/l (Wet resin) | MMOL/L(Wet resin)≥2000 |